Water Atomized Iron Powder Material
Pure Iron Powder
Low Alloy Steel Powder
Easy Cutting Steel Powder
Stainless Steel Powder
High Alloy Steel Powder
Iron Powder for Welding Rod
Iron Powder for Magnetism
Super-fine Iron Powder
Ni Powder
Copper-based Alloy Powder
Sintered CuPb Alloy Powder
High-strength Copper Powder
Sn-Bronze Alloy Powder
Sn-Bronze Mixed Powder
Atomized Bronze Powder
Atomized Copper Powder
Sn Powder
Pb Powder
 
·Partially Alloyed Steel Powder For High Strength Applications(2300WB)
Properties of Powder
Chemical Composition% Ni 4 Cu 1.5 Mo 0.5
Apparent Density g/cm3 2.98 Compressibility*
g/cm3
500MPa 6.90
Flow Rate s/50g 26.9 600Mpa 7.05
Particle Size Distribution -180+250 -150+106 -106+75 -75+63 -63+45 -45
0.5 22.5 21 12 19 25
*mixed with 0.75%Zn-St
Characteristics:1)High Compressibility ;2)The sintering atmosphere is changeable to demand as adding Ni.3)It can reach higher intensity and hardness without heat treatment;4)Sintering temperature can be controlled according to intensity demand. Applications:1) Auto sintered parts such as clutch gear, oil pump washer;2)other sintered mechanical components.



·Partially Alloyed Steel Powder For High Strength Applications(1300WB)
 Mechanical Properties of Powder After Sintering
Properties of Powder
Chemical Composition% Ni 2 Cu 1.5 Mo 0.5
Apparent Density g/cm3 2.98 Compressibility*
g/cm3
500MPa 6.93
Flow Rate s/50g 26.9 600Mpa 7.10
Particle Size Distribution -180+250 -150+106 -106+75 -75+63 -63+45 -45
0.5 22.5 21 12 19 25
*mixed with 0.75%Zn-St
Characteristics:1)High Compressibility ;2)The sintering atmosphere is changeable to demand as adding Ni.3)It can reach higher intensity and hardness without heat treatment
Applications:1)Auto parts such as gear 2)other sintered mechanical components.



·Completely Alloyed Steel Powder For High Strength Applications(1300WA)
Mechanical Properties of Powder After Sintering
Properties of Powder
Chemical Composition% Ni 1.7-2.2 Mo 0.4-0.6  
Apparent Density g/cm3 2.98 Compressibility*
g/cm3
500MPa 6.73
Flow Rate s/50g 26.5 600Mpa 6.94
Particle Size Distribution -180+250 -150+106 -106+75 -75+63 -63+45 -45
0.5 22.5 21 12 19 25
*mixed with 0.75%Zn-St
Characteristics:1) High Quenching Degree2)It can reach higher intensity and without heat treatment
Applications:1)Auto parts 2)Medium-high density sintered structural parts


300W Water Atomized Pure Iron Powder Sintered Material   Properties

Code Name(MPIF Standard)

Composition of Mixed Powde(%)
Sintering Density(g/cm3)
Dimensional Change 1) Rate(%)
Transverse Rupture Strength(MPa)
Extreme Tensile Strength(MPa)
Yield Strength(MPa)
Tensile Ratio%
Apparent Hardness HRB
Fe
Cu
Ni
Graphite
Zinc Stearate
Sintered Carbon Steel
F-0000
Balance
-
-
0.0
0.5
6.8
-0.06
445
205
141
10 
27 
Balance
-
-
0.0
0.5
7.0
-0.04
535
230
152
13 
37 
Balance
-
-
0.3
0.5
6.8
+0.02
493
243
170
7 
38 
Balance
-
-
0.3
0.5
7.0
+0.07
610
276
186
9 
46 
F-0005
Balance
-
-
0.6
0.5
6.8
+0.09
635
305
221
4 
55 
Balance
-
-
0.6
0.5
7.0
+0.13
722
342
237
5 
61 
F-0008
Balance
-
-
0.9
0.5
6.8
+0.14
737
359
264
3 
68 
Balance
-
-
0.9
0.5
7.0
+0.17
826
405
285
3 
74 
Sintered Carbon Steel
FC-0200
Balance
2.0
-
0.0
0.5
6.8
+0.56
661
248
145
3 
56 
Balance
2.0
-
0.0
0.5
7.0
+0.58
745
276
165
5 
63 
FC-0205
Balance
2.0
-
0.6
0.5
6.8
+0.39
944
455
358
2 
80 
Balance
2.0
-
0.6
0.5
7.0
+0.42
1096
503
386
3 
86 
FC-0208
Balance
2.0
-
0.9
0.5
6.8
+0.22
1082
538
448
2 
88 
Balance
2.0
-
0.9
0.5
7.0
+0.30
1255
600
489
2 
92 
Sintered Carbon Steel
FN-0200
Balance
-
2.0
0.3
0.5
6.8
-0.12
634
269
159
2 
49 
Balance
-
2.0
0.3
0.5
7.0
-0.09
717
303
165
5 
55 
FN-0205
Balance
-
2.0
0.6
0.5
6.8
-0.07
717
303
214
2 
64 
Balance
-
2.0
0.6
0.5
7.0
-0.01
841
372
234
3 
67 
FN-0208
Balance
-
2.0
0.9
0.5
6.8
+0.02
807
352
290
1 
73 
Balance
-
2.0
0.9
0.5
7.0
+0.07
965
421
317
1 
79 
FN-0405
Balance
-
4.0
0.6
0.5
6.8
-0.11
820
296
255
<1 
77 
Balance
-
4.0
0.6
0.5
7.0
-0.06
1007
379
290
1 
81 
FN-0408
Balance
-
4.0
0.9
0.5
6.8
-0.10
800
303
283
<1 
78 
Balance
-
4.0
0.9
0.5
7.0
-0.14
1000
400
331
<1 
84 
Sintering in an atmosphere of endothermal coal gas for 35 minutes at 1120°C 。
1)Dimensional change is from sintered die size.


300W Water Atomized Pure Iron Powder Sintered Material Properties after Heat
Code Name(MPIF Standard)
Composition of Mixed Powder(%)
Sintering Density(g/cm3)
Transverse Rupture Strength(MPa)
Extreme Tensile Strength(MPa)
Impact Strength(J)
Apparent Hardness
HRB
Fe
Cu
Ni
Graphite
Zinc Stearate
Sintered Copper Steel1)
FC-0205HT
Balance
2.0
-
0.6
0.5
6.8
1172
789
-
27
Balance
2.0
-
0.6
0.5
7.0
1344
869
-
30
Balance
3.0
-
0.6
0.5
6.8
1234
765
-
27
Balance
3.0
-
0.6
0.5
7.0
1372
882
-
29
FC-0208HT
Balance
2.0
-
0.9
0.5
6.8
1358
862
-
35
Balance
2.0
-
0.9
0.5
7.0
1593
1027
-
40
Balance
3.0
-
0.9
0.5
6.8
1434
848
-
34
Balance
3.0
-
0.9
0.5
7.0
1744
979
-
38
Sintered Nickel Steel2)
FN-0205HT
Balance
-
2.0
0.6
0.5
6.8
1158
885
8
37
Balance
-
2.0
0.6
0.5
7.0
1358
1013
8
42
FN-0405HT
Balance
-
4.0
0.6
0.5
6.8
1200
834
9
26
Balance
-
4.0
0.6
0.5
7.0
1462
965
12
31
Sintering in an atmosphere of endothermal coal gas for 30 minutes at 1120°C.
   Heat Treating: for 15minutes at 845°C .
   1) Oil Quenching, tempering for 60 minutes at 175°C.
   2)Oil Quenching, tempering for 60 minutes at 260°C.


🔥正规现金十大赌博平台-十大正规赌博网站排名-十大正规赌博网站公司
Addr:Daciyan Town of Jiande City, Zhejiang Province, China         Tel:0571-64560576        Fax:0571-64560177
Copyright © 2010 Hangzhou Yitong New Material Co., LTD  All rights service               Design by:China P/M Business Network